Semiconductor device and method of fabricating the same

ABSTRACT

A semiconductor device includes a semiconductor substrate, a gate stack, an air spacer, a first spacer, a second spacer, a sacrificial layer, and a contact plug. The gate stack is on the semiconductor substrate. The air spacer is around the gate stack. The first spacer is around the air spacer. The second spacer is on the air spacer and the first spacer. The sacrificial layer is on the gate stack, and an etching selectivity between the second spacer and the sacrificial layer is in a range from about 10 to about 30. The contact plug lands on the second spacer and the gate stack.

PRIORITY CLAIM AND CROSS-REFERENCE

This application claims priority to U.S. Provisional Application Ser. No. 62/864,004, filed Jun. 20, 2019, which is herein incorporated by reference.

BACKGROUND

The semiconductor integrated circuit (IC) industry has experienced rapid growth. Technological advances in integrated circuit materials and design have produced generations of integrated circuits. Each generation has smaller and more complex circuits than the previous generation. However, these advances have increased the complexity of processing and manufacturing integrated circuits. In the course of integrated circuit evolution, functional density (i.e., the number of interconnected devices per chip area) has generally increased while geometric size (i.e., the smallest component (or line) that can be created using a fabrication process) has decreased. This scaling-down process generally provides benefits by increasing production efficiency and lowering associated costs. However, since feature sizes continue to decrease, fabrication processes continue to become more difficult to perform. Therefore, it is a challenge to form reliable semiconductor devices at smaller and smaller sizes.

BRIEF DESCRIPTION OF THE DRAWINGS

Aspects of the present disclosure are best understood from the following detailed description when read with the accompanying figures. It is noted that, in accordance with the standard practice in the industry, various features are not drawn to scale. In fact, the dimensions of the various features may be arbitrarily increased or reduced for clarity of discussion.

FIG. 1 is a flow chart illustrating a method of fabricating a semiconductor device in accordance with some embodiments of the present disclosure;

FIGS. 2-22 are cross-sectional views illustrating a method for fabricating a semiconductor device at various stages in accordance with some embodiments of the present disclosure;

FIG. 23 is a flow chart illustrating a method of fabricating a semiconductor device in accordance with other embodiments of the present disclosure; and

FIGS. 24-44 are cross-sectional views illustrating a method for fabricating a semiconductor device at various stages in accordance with other embodiments of the present disclosure.

DETAILED DESCRIPTION

The following disclosure provides many different embodiments, or examples, for implementing different features of the provided subject matter. Specific examples of components and arrangements are described below to simplify the present disclosure. These are, of course, merely examples and are not intended to be limiting. For example, the formation of a first feature over or on a second feature in the description that follows may include embodiments in which the first and second features are formed in direct contact, and may also include embodiments in which additional features may be formed between the first and second features, such that the first and second features may not be in direct contact. In addition, the present disclosure may repeat reference numerals and/or letters in the various examples. This repetition is for the purpose of simplicity and clarity and does not in itself dictate a relationship between the various embodiments and/or configurations discussed.

Further, spatially relative terms, such as “beneath,” “below,” “lower,” “above,” “upper” and the like, may be used herein for ease of description to describe one element or feature's relationship to another element(s) or feature(s) as illustrated in the figures. The spatially relative terms are intended to encompass different orientations of the device in use or operation in addition to the orientation depicted in the figures. The apparatus may be otherwise oriented (rotated 90 degrees or at other orientations) and the spatially relative descriptors used herein may likewise be interpreted accordingly.

The fins may be patterned by any suitable method. For example, the fins may be patterned using one or more photolithography processes, including double-patterning or multi-patterning processes. Generally, double-patterning or multi-patterning processes combine photolithography and self-aligned processes, allowing patterns to be created that have, for example, pitches smaller than what is otherwise obtainable using a single, direct photolithography process. For example, in one embodiment, a sacrificial layer is formed over a substrate and patterned using a photolithography process. Spacers are formed alongside the patterned sacrificial layer using a self-aligned process. The sacrificial layer is then removed, and the remaining spacers may then be used to pattern the fins.

FIG. 1 is a flow chart illustrating a method of fabricating a semiconductor device in accordance with some embodiments of the present disclosure. The method begins with block 10 in which an interlayer dielectric layer and a gate stack are formed on a semiconductor substrate. The method continues with block 12 in which an air spacer and a first spacer are formed to surround a sidewall of the gate stack, wherein the first spacer is on a sidewall of the interlayer dielectric layer, and the air spacer is between the gate stack and the first spacer. The method continues with block 14 in which a second spacer is formed on the first spacer and the air spacer, wherein the second spacer has a portion in contact with a sidewall of the first spacer. The method continues with block 16 in which a first contact hole is formed to land on the second spacer and the gate stack, wherein a sidewall of the first contact hole is defined by the second spacer. The method continues with block 18 in which the first contact hole is filled with a conductive material.

As employed in the present disclosure, the semiconductor device 100 refers to any fin-based, multi-gate transistor. The semiconductor device 100 may be included in a microprocessor, memory cell, and/or other integrated circuit (IC). It is understood that additional processes may be provided before, during, and after the method of FIG. 1, and that some other processes may only be briefly described herein. Also, FIGS. 1 through 22 are simplified for a better understanding of the inventive concepts of the present disclosure. For example, although the figures illustrate the semiconductor device 100, it is understood the IC may include a number of other devices including resistors, capacitors, inductors, fuses, etc.

Reference is made to FIGS. 2-22, which are cross-sectional views illustrating the method for fabricating the semiconductor device 100 at various stages in accordance with some embodiments of the present disclosure.

Reference is made to FIG. 2. A substrate with a fin structure 110 is provided. The fin structure 110 is formed by etching into the substrate. In some embodiments, the substrate may be a semiconductor wafer such as a silicon wafer. Alternatively or additionally, the substrate may include elementary semiconductor materials, compound semiconductor materials, and/or alloy semiconductor materials. Examples of the elementary semiconductor materials may be, but are not limited to, crystal silicon, polycrystalline silicon, amorphous silicon, germanium, and/or diamond. Examples of the compound semiconductor materials may be, but are not limited to, silicon carbide, gallium arsenic, gallium phosphide, indium phosphide, indium arsenide, and/or indium antimonide. Examples of the alloy semiconductor materials may be, but are not limited to, SiGe, GaAsP, AlInAs, AlGaAs, GaInAs, GaInP.

Afterwards, dummy gate structures, such as a first dummy gate structure 120 a and a second dummy gate structure 120 b are formed cross over the fin structure 110. The first dummy gate structure 120 a includes a gate dielectric layer 122 a, a dummy gate electrode layer 124 a, and a hard mask 126 a. The second dummy gate structure 120 b includes a gate dielectric layer 122 b, a dummy gate electrode layer 124 b, and a hard mask 126 b. The formation of the gate dielectric layers 122 a and 122 b and the dummy gate electrode layers 124 a and 124 b includes depositing a gate dielectric material layer (not shown) over the fin structure 110, depositing a dummy gate material layer (not shown) over the gate dielectric material layer, and patterning the dummy gate material layer and the gate dielectric material layer by an etching process, in accordance with some embodiments. The gate dielectric material layer and the dummy gate material layer may be deposited using a chemical vapor deposition (CVD) process. The hard masks 126 a and 126 b are formed over portions of the dummy gate material layer during the etching process, such that portions of the gate dielectric material layer and the dummy gate material layer not covered by the hard masks 126 a and 126 b are removed. In some embodiments, the material of the gate dielectric layers 122 a and 122 b includes silicon oxide, and the material of the dummy gate electrode layer 124 a and 124 b includes polysilicon.

Reference is made to FIG. 3. Low-k spacers 132 a and 132 b are respectively formed on opposite sidewalls of the first and second dummy gate structures 120 a and 120 b. The low-k spacers 132 a and 132 b may be formed by conformally depositing a low-k spacer material layer (not shown) followed by an anisotropic etching (e.g., lateral etching) process. An example of a low-k spacer material may be a porous low-k material including SiOC, SiOCN, other suitable materials, or combinations thereof. After the low-k spacers 132 a and 132 b are formed, the first spacers 134 a and 134 b are then respectively formed adjacent to the low-k spacers 132 a and 132 b. The first spacers 134 a and 134 b may be formed by conformally depositing a first spacer material layer (not shown) followed by an anisotropic etching (e.g., lateral etching) process. An example of the first spacer material layer may be a non-porous material including nitride. As a result, the low-k spacers 132 a and 132 b are formed between the first and second dummy gate structures 120 a and 120 b and the first spacers 134 a and 134 b.

After the formation of the low-k spacers 132 a and 132 b and the first spacers 134 a and 134 b, a source/drain region 112 is formed in the substrate between the first and second dummy gate structures 120 a and 120 b. Although only one source/drain region 112 is illustrated in FIG. 3, a plurality of source/drain regions may be formed on opposite sides of the first and second dummy gate structures 120 a and 120 b. A dimension of the source/drain region 112 is defined by the first spacers 134 a and 134 b. In some embodiments, the source/drain region 112 may include the introduction of suitable dopant types, such as n-type or p-type dopants. The formation of the source/drain region 112 includes halo (or pocket) and/or low-dose drain (LDD) implantation, source/drain implantation, source/drain activation and/or other suitable processes. In other embodiments, the source/drain regions may include raised source/drain regions, strained regions, epitaxially grown regions, and/or other suitable techniques. In further embodiments, the source/drain activation process may include a rapid thermal annealing.

Reference is made to FIG. 4. A first interlayer dielectric (ILD) layer 140 is formed between the first and second dummy gate structures 120 a and 120 b, such that the first spacers 134 a and 134 b are on sidewalls of the ILD layer 140. The first ILD layer 140 may be formed by a CVD process, a high-density plasma (HDP) process, the like, or combinations thereof. In some embodiments, the first ILD layer 140 may be optionally planarized to lower its top surface to a level of first and second dummy gate structures 120 a and 120 b. For example, the first ILD layer 140 is planarized by using a chemical mechanical planarization (CMP) process. In other embodiments, other planarization techniques may be used, such as etching. The material of the first ILD layer 140 may include a dielectric material, such as a non-porous oxide material.

Reference is made to FIG. 5. The hard masks 126 a and 126 b (see FIG. 4) are removed after the first ILD layer 140 is formed. The dummy gate electrode layer 124 a and 124 b (see FIG. 4) are then removed to respectively form recesses 135 a and 135 b between the low-k spacers 132 a and 132 b. The removal of the dummy gate electrode layer 124 a and 124 b may be performed by a dry etching process which is selective to the material of the dummy gate electrode layer 124 a and 124 b. For example, if the dummy gate electrode layer 124 a and 124 b includes polysilicon, a dry etch using NF, SF, Cl, HBr, the like, or combinations thereof; or a wet etch using NH₄OH, tetramethylammonium hydroxide (TMAH), the like, or combinations thereof may be performed. In some embodiments, the etching of the dummy gate electrode layer 124 a and 124 b may stop at the gate dielectric layers 122 a and 122 b. As a result, the recesses 135 a and 135 b are formed to respectively expose the gate dielectric layers 122 a and 122 b. In alternative embodiments, the gate dielectric layers 122 a and 122 b may be removed along with the dummy gate electrode layer 124 a and 124 b. Diameters of the recesses 135 a and 135 b are respectively defined by sidewalls of the low-k spacers 132 a and 132 b.

Reference is made to FIG. 6. Gate stacks 150 a and 150 b are respectively formed in the recesses 135 a and 135 b (see FIG. 5). In some embodiments, the gate stacks 150 a and 150 b may include a single material or any combination of layers and different materials as may be appropriate. For example, the gate stacks 150 a and 150 b may include work function layers 152 a and 152 b and metal gate electrode layers 154 a and 154 b. The work function layers 152 a and 152 b and the metal gate electrode layers 154 a and 154 b are sequentially formed in the recesses 135 a and 135 b. For example, a work function material layer (not shown) is conformally formed in the recesses 135 a and 135 b covering the gate dielectric layers 122 a and 122 b and sidewalls of the low-k spacers 132 a and 132 b, and a metal gate electrode material layer (not shown) is then deposited, such as by a CVD process, a physical vapor deposition (PVD) process, the like, or a combination thereof, to fill in the recesses 135 a and 135 b. A planarization process, such as a CMP process, may be performed to remove excess portions of the metal gate electrode material layer and the work function material layer, in which the excess portions are over the top of the first ILD layer 140, the low-k spacers 132 a and 132 b, and the first spacers 134 a and 134 b, thus resulting in a replacement of the dummy gate electrode layer 124 a and 124 b (see FIG. 4) and the hard masks 126 a and 126 b (see FIG. 4) with the gate stacks 150 a and 150 b including the work function layers 152 a and 152 b and the metal gate electrode layers 154 a and 154 b. The work function layers 152 a and 152 b may be tuned to have a proper work function. For example, if a p-type work function metal (p-metal) for a p-metal oxide semiconductor (pMOS) device is desired, p-type work function materials may be used. On the other hand, if an n-type work function metal (n-metal) for n-metal oxide semiconductor (nMOS) devices is desired, n-type work function materials may be used. The materials of the metal gate electrode layers 154 a and 154 b may include elemental metal, an alloy of metals, multiple layers of elemental metal, or combinations thereof, and can include tungsten (W), aluminium (Al), cobalt (Co), ruthenium (Ru), the like, or combinations thereof.

Reference is made to FIG. 7. The gate stacks 150 a and 150 b are etched back to a level approximately half the height of the low-k spacers 132 a and 132 b and the first spacers 134 a and 134 b. A mask layer (not shown) may be formed over the first ILD layer 140, the low-k spacers 132 a and 132 b, and the first spacers 134 a and 134 b during the etching process. As a result, the recesses 135 a and 135 b are reappeared with a shallower depth, and upper portions of the low-k spacers 132 a and 132 b are exposed by the work function layers 152 a and 152 b of the gate stacks 150 a and 150 b.

Reference is made to FIG. 8. The upper portions of the low-k spacers 132 a and 132 b and upper portions of the first spacers 134 a and 134 b are removed by an anisotropic etching (e.g., lateral etching) process. In some embodiments, the low-k spacers 132 a and 132 b and the first spacers 134 a and 134 b are etched back to a level approximately the height of the gate stacks 150 a and 150 b. A mask layer (not shown) may be formed over the first ILD layer 140 during the etching process. Furthermore, since the anisotropic etching process has a milder impact to the underlying gate stacks 150 a and 150 b, the gate stacks 150 a and 150 b are retained. As a result, recesses 137 a and 137 b are formed between the adjacent first ILD layers 140. Stated differently, diameters of the recesses 137 a and 137 b are defined by sidewalls of the adjacent first ILD layers 140, such that the diameters of the recesses 137 a and 137 b are larger than the diameters of the recesses 135 a and 135 b (see FIG. 7) which are defined by sidewalls of the low-k spacers 132 a and 132 b.

Reference is made to FIG. 9. The remaining low-k spacers 132 a and 132 b are then removed, such that spaces 136 are formed between the gate stacks 150 a and 150 b and the first spacers 134 a and 134 b, and portions of the fin structure 110 are exposed from the spaces 136. The removal of the low-k spacers 132 a and 132 b may be performed by an etching process, such as a wet etching process or a dry etching process. In some embodiments, the material of the low-k spacers 132 a and 132 b, such as SiOC or SiOCN, gives an etching selectivity relative to the material of the first ILD layer 140 and the first spacers 134 a and 134 b including oxide and nitride, respectively. In alternative embodiments, the porous material of the low-k spacers 132 a and 132 b gives an etching selectivity relative to the non-porous materials of the first ILD layer 140 and the first spacers 134 a and 134 b. As a result, sidewalls of the first spacers 134 a and 134 b, sidewalls of the gate stacks 150 a and 150 b, and sidewalls of the gate dielectric layers 122 a and 122 b are exposed from the spaces 136.

Reference is made to FIG. 10. A second spacer material 138 is conformally formed on the semiconductor structure 100 shown in FIG. 9 by deposition. For example, the second spacer material 138 covers the first ILD layer 140, the gate stacks 150 a and 150 b, the first spacers 132 a and 132 b, and the spaces 136 (see FIG. 9), and is formed on sidewalls of the first ILD layer 140. In some embodiments, the second spacer material 138 has portions 138′ embedded into the spaces 136 and in contact with sidewalls of the gate stacks 150 a and 150 b and sidewalls of the first spacers 134 a and 134 b. Hence, spaces 136 are reappeared with a smaller height and are referred to as air spacers 136 a and 136 b in the following descriptions. The air spacers 136 a and 136 b having an extremely low-k characteristic are formed to reduce parasitic capacitance of the semiconductor device 100. Since portions 138′ of the second spacer material 138 extend into the spaces 136 during the deposition, a height of the air spacers 136 a and 136 b is smaller than that of the first spacers 134 a and 134 b and that of the gate stacks 150 a and 150 b, and top surfaces of the air spacers 136 a and 136 b are lower than that of the gate stacks 150 a and 150 b. Examples of the second spacer material 138 include, but are not limited to, high-k dielectric materials including AlO, AlN, AlON, ZrO, ZrN, ZrAlO, HfO, the like, or combinations thereof; or non-porous and low-k materials including SiO, SiN, SiC, SiCN, SiON, SiOCN, the like, or combinations thereof.

Since a thickness T1 of the removed low-k spacers 132 a and 132 b (see FIG. 3) is in a range from about 1 nm to about 10 nm, a width W1 of the spaces 136 (see FIG. 9) is in a range from about 1 nm to about 10 nm, and a width W1 of the air spacers 136 a and 136 b is in a range from about 1 nm to about 10 nm. In some embodiments, a length L1 of the portions 138′ of the second spacer material 138 extending into the spaces 136 is controlled by the width W1 of the spaces 136 which is in a range from about 1 nm to about 10 nm. For example, if the width W1 of the spaces 136 is larger than about 10 nm, the second spacer material 138 may easily fill in the spaces 136 at a large extent during the deposition, resulting in a decrease in height of the air spacers 136 a and 136 b, or even an entire filling-up of the spaces 136. On the other hand, if the width W1 of the spaces 136 is smaller than about 1 nm, which means the thickness T1 of the removed low-k spacer 132 a and 132 b is smaller than about 1 nm, the formation of the spaces 136 may be difficult since bottom portions of the low-k spacers 132 a and 132 b may be difficult to remove due to the small thickness T1. In some embodiments, the length L1 of the portions 138′ of the second spacer material 138 extending into the spaces 136 is in a range from about 0.5 nm to about 5 nm to ensure that the height of the air spacers 136 a and 136 b is in an appropriate range to maintain their functionality (i.e., to reduce parasitic capacitance of the semiconductor device 100).

Reference is made to FIG. 11. An anisotropic etching (e.g., lateral etching) process is performed such that portions of the second spacer material 138 (see FIG. 10) are removed. For example, portions of the second spacer material 138 covering the gate stacks 150 a and 150 b are removed, and portions of the second spacer material 138 above the top surface of the first ILD layer 140 are also removed. As a result, second spacers 138 a and 138 b are formed standing on the first spacers 132 a and 132 b and the air spacers 136 a and 136 b, and recesses 139 a and 139 b are respectively formed between the second spacers 138 a and 138 b, that is, diameters of the recesses 139 a and 139 b are respectively defined by sidewalls of the second spacers 138 a and 138 b. The gate stacks 150 a and 150 b are exposed by the second spacers 138 a and 138 b, and top surfaces of the second spacers 138 a and 138 b are coplanar with the top surface of the first ILD layer 140. In some embodiments, a thickness T2 of the second spacers 138 a and 138 b is in a range from about 1 nm to about 10 nm. Furthermore, the thickness T2 of the second spacers 138 a and 138 b should be larger than the width W1 of air spacers 136 a and 136 b to ensure the air spacers 136 a and 136 b being entirely sealed. If the thickness T2 of the second spacers 138 a and 138 b is smaller than about 1 nm, the air spacers 136 a and 136 b may possibly be exposed, resulting in a fragile structure of the semiconductor device 100; if the thickness T2 of the second spacers 138 a and 138 b is larger than about 10 nm, the size of the semiconductor device 100 would be increased accordingly.

After this step, the second spacers 138 a and 138 b including first portions 138 a′ and 138 b′ and second portions 138 a″ and 138 b″ are formed. The first portions 138 a′ and 138 b′ are the portions 138′ of the second spacer material 138 extending into the spaces 136 (see FIG. 8) and are in contact with sidewalls of the first spacers 134 a and 134 b and sidewalls of the gate stacks 150 a and 150 b. The second portions 138 a″ and 138 b″ are on the first portions 138 a′ and 138 b′ of the second spacers 138 a and 138 b and the first spacers 134 a and 134 b.

Reference is made to FIG. 12. A first sacrificial material layer 156 is deposited over the semiconductor structure 100 shown in FIG. 11 by, for example, a CVD process, a plasma enhanced chemical vapor deposition (PECVD) process, the like, or combinations thereof. For example, the first sacrificial material layer 156 is filled in the recesses 139 a and 139 b (see FIG. 11), and formed over the second spacers 138 a and 138 b and the first ILD layer 140. The material of the first sacrificial material layer 156 may include a porous and low-k material. Examples of the porous and low-k material are, but are not limited to, SiO, SiN, SiC, SiCN, SiON, SiOCN, the like, or combinations thereof. Such a material give an etching selectivity relative to the materials of the second spacers 138 a and 138 b (i.e., the second spacer material 138), which include, but are not limited to, high-k dielectric materials including AlO, AlN, AlON, ZrO, ZrN, ZrAlO, HfO, the like, or combinations thereof; or non-porous and low-k materials including SiO, SiN, SiC, SiCN, SiON, SiOCN, the like, or combinations thereof.

Reference is made to FIG. 13. A planarization process is performed to lower the first sacrificial material layer 156 and to expose the second spacers 138 a and 138 b. In some embodiments, the first sacrificial material layer 156 is planarized by using a CMP process. In other embodiments, other planarization techniques may be used, such as etching. As a result, first sacrificial layers 156 a and 156 b are respectively formed in the recesses 139 a and 139 b (see FIG. 11) and are respectively formed between the second spacers 138 a and 138 b. Additionally, top surfaces of the first sacrificial layers 156 a and 156 b are coplanar with top surfaces of the second spacers 138 a and 138 b and the top surface of the first ILD layer 140.

Reference is made to FIG. 14. The first ILD layer 140 is removed by an etching process. A mask layer (not shown) may be formed over the first sacrificial layer 156 a and 156 b and the second spacers 138 a and 138 b during the etching process. The removal of the first ILD layer 140 results in a formation of a recess 142 above the underlying source/drain region 112, that is, an exposure of the underlying source/drain region 112 from the recess 142.

Reference is made to FIG. 15. A first barrier layer 144 and a bottom conductive feature 172 are sequentially formed in the recess 142 (see FIG. 14). In some embodiments, a first barrier material layer (not shown) is conformally formed in the recess 142 covering the source/drain region 112, sidewalls of the first spacers 134 a and 134 b, and sidewalls of the second spacers 138 a and 138 b, and a bottom conductive material (not shown) is then deposited, such as by a CVD process, a PVD process, a PECVD process, a low pressure CVD (LPCVD) process, the like, or a combination thereof, to fill in the recess 142. A planarization process, such as a CMP process, may be performed to remove excess portions of the first barrier material layer and the bottom conductive material, and thus resulting in a replacement of the first ILD layer 140 with the first barrier layer 144 and the bottom conductive feature 172. In some embodiments, the first barrier material layer includes, but are not limited to, cobalt (Co), silver (Ag), aluminium (Al), zinc (Zn), calcium (Ca), gold (Au), magnesium (Mg), tungsten (W), molybdenum (Mo), nickel (Ni), chromium (Cr), the like, or combinations thereof. Additionally, the bottom conductive material includes conductive materials, such as tungsten (W), aluminium (Al), cobalt (Co), ruthenium (Ru), the like, or combinations thereof, which form an electrical connection to the source/drain region 112. In some embodiments, other layers such as a work function layer and/or a capping layer may be formed in the recess 142, but the present disclosure is not limited in this regard.

Reference is made to FIG. 16. The first barrier layer 144 and the bottom conductive feature 172 are etched back. A mask layer (not shown) may be formed over the first sacrificial layer 156 a and 156 b and the second spacers 138 a and 138 b during the etching process. As a result, a recess 146 is formed over the first barrier layer 144 and the bottom conductive feature 172, and a diameter of the recess 146 is defined by the sidewalls of the second portions 138 a″ and 138 b″ of the second spacers 138 a and 138 b. In some embodiments, a top surface of the bottom conductive feature 172 is coplanar with the top surfaces of the gate stacks 150 a and 150 b. In alternative embodiments, the top surface of the bottom conductive feature 172 is higher or lower than the top surfaces of the gate stacks 150 a and 150 b. Since the air spacers 136 a and 136 b are between the bottom conductive feature 172 and the gate stacks 150 a and 150 b, the air spacers 136 a and 136 b with an extremely low-k characteristic can effectively reduce the parasitic capacitance between the gate stacks 150 a and 150 b and the bottom conductive features 172.

Reference is made to FIG. 17. A second sacrificial material layer (not shown) is deposited over the semiconductor structure 100 shown in FIG. 16 by, for example, a CVD process, a PECVD process, the like, or combinations thereof. For example, the second sacrificial material layer is filled in the recess 146 (see FIG. 16), and formed over the second spacers 138 a and 138 b and the first sacrificial layers 156 a and 156 b. After that, a planarization process is then performed to lower the second sacrificial material layer and to expose the second spacers 138 a and 138 b and the first sacrificial layers 156 a and 156 b. In some embodiments, the second sacrificial material layer is planarized by using a CMP process. In other embodiments, other planarization techniques may be used, such as etching. As a result, a second sacrificial layer 174 is formed in the recess 146 to cover the bottom conductive feature 172 and the first barrier layer 144. A top surface of the second sacrificial layer 174 is coplanar with top surfaces of the second spacers 138 a and 138 b and top surfaces of the first sacrificial layers 156 a and 156 b. The material of the second sacrificial layer 174 (i.e., second sacrificial material layer) may include a porous and low-k material. Examples of the porous and low-k material are, but are not limited to, SiO, SiN, SiC, SiCN, SiON, SiOCN, the like, or combinations thereof. Such a material give an etching selectivity relative to the materials of the second spacers 138 a and 138 b (i.e., the second spacer material 138), which include, but are not limited to, high-k dielectric materials including AlO, AlN, AlON, ZrO, ZrN, ZrAlO, HfO, the like, or combinations thereof; or non-porous and low-k materials including SiO, SiN, SiC, SiCN, SiON, SiOCN, the like, or combinations thereof.

Reference is made to FIG. 18. A contact etch stop layer (CESL) 180 and a second ILD layer 182 are formed to blanket cover the first sacrificial layers 156 a and 156 b, the second sacrificial layer 174, and the second spacers 138 a and 138 b by a deposition process such as, for example, a CVD process, a PECVD process, a LPCVD process, the like, or a combination thereof. The material of the contact etch stop layer 280 includes, for example, SiO, SiN, SiC, SiCN, SiON, SiOCN, the like, or combinations thereof. Such a material give an etching selectivity relative to the materials of the second spacers 138 a and 138 b (i.e., the second spacer material 138), which include, but are not limited to, high-k dielectric materials including AlO, AlN, AlON, ZrO, ZrN, ZrAlO, HfO, the like, or combinations thereof; or non-porous and low-k materials including SiO, SiN, SiC, SiCN, SiON, SiOCN, the like, or combinations thereof. Additionally, the material of the second ILD layer 182 may include the same material as the material of the first ILD layer 140, which will not be repeated hereinafter.

Reference is made to FIG. 19. A first contact hole 183 is formed penetrating through the second ILD layer 182, the CESL 180, and the first sacrificial layer 156 a. The first contact hole 183 may be formed using acceptable photolithography and etching techniques by removing portions of the second ILD layer 182, the CESL 180, and the first sacrificial layer 156 a. Since the second spacer 138 a has an etching selectivity in a range from about 10 to about 30 relative to the CESL 180 and the first sacrificial layer 156 a, the etching process may stop at the second spacer 138 a to prevent a further removal of the second spacer 138 a. Hence, the first contact hole 183 is formed to expose a portion of the top surface of the gate stack 150 a, a portion of the top surface of the second spacer 138 a, and a portion of the sidewall of the second spacer 138 a, resulting in a staircase configuration of the first contact hole 183. Stated differently, the first contact hole 183 has an upper portion 183 a and a lower portion 183 b, in which a diameter of the upper portion 183 a is larger than that of the lower portion 183 b, and a sidewall of the lower portion 183 b of the first contact hole 183 is defined by the sidewall of the second spacer 138 a. Furthermore, a sidewall of the second ILD layer 182 is coplanar with a sidewall of the CESL 180 and a sidewall of the first sacrificial layer 156 a.

Reference is made to FIG. 20. A second contact hole 185 is formed penetrating through the second ILD layer 182, the CESL 180, and the second sacrificial layer 174. The second contact hole 185 may be formed using acceptable photolithography and etching techniques by removing portions of the second ILD layer 182, the CESL 180, and the second sacrificial layer 174. Since the second spacer 138 b has an etching selectivity in a range from about 10 to about 30 relative to the CESL 180 and the second sacrificial layer 174, the etching process may stop at the second spacer 138 b to prevent a further removal of the second spacer 138 b. Hence, the second contact hole 185 is formed to expose a portion of the top surface of the bottom conductive feature 172, a portion of the top surface of the first barrier layer 144, a portion of the top surface of the second spacer 138 b, and a portion of the sidewall of the second spacer 138 b, resulting in a staircase configuration of the second contact hole 185. Stated differently, the second contact hole 185 has an upper portion 185 a and a lower portion 185 b, in which a diameter of the upper portion 185 a is larger than that of the lower portion 185 b, and a sidewall of the lower portion 185 b of the second contact hole 185 is defined by the sidewall of the second spacer 138 b. Furthermore, a sidewall of the second ILD layer 182 is coplanar with a sidewall of the CESL 180 and a sidewall of the second sacrificial layer 174.

Since the second spacers 138 a and 138 b has an etching selectivity in a range from about 10 to about 30 relative to the CESL 180, the first sacrificial layers 156 a and 156 b, and the second sacrificial layer 174, the first contact hole 183 and the second contact hole 185 do not penetrate through the second spacers 138 a and 138 b. Hence, the first spacers 134 a and 134 b and the air spacers 136 a and 136 b are not exposed and are well protected during the etching process due to the etching resistance provided by the second spacer 138 a and 138 b. If the etching selectivity of second spacer 138 a and 138 b relative to the CESL 180, the first sacrificial layers 156 a and 156 b, and the second sacrificial layer 174 is smaller than about 10, the etching process may lead to unwanted consumption of the underlying components, such as the first spacers 132 a and 132 b, thereby causing a risk for the first contact plug and the second contact plug (which will be formed respectively in the first contact hole 183 and the second contact hole 185 in subsequent steps) to be respectively in contact with the bottom conductive feature 172 and the gate stack 150 b, hence enhancing a chance for shorting.

Additionally, the length L2 of the second portions 138 a″ and 138 b″ of the second spacers 138 a and 138 b which is in a range from about 1 nm to about 10 nm also contributes to the formation of the first contact hole 183 and the second contact hole 185. Specifically, if the length L2 of the second portions 138 a″ and 138 b″ of the second spacers 138 a and 138 b is smaller than about 1 nm, the etching process may easily lead to unwanted consumption of the underlying components, such as the first spacers 132 a and 132 b, thereby causing a risk for the first contact plug and the second contact plug (which will be formed respectively in the first contact hole 183 and the second contact hole 185 in subsequent steps) to be respectively in contact with the bottom conductive feature 172 and the gate stack 150 b, hence enhancing a chance for shorting. On the other hand, if the length L2 of the second portions 138 a″ and 138 b″ is larger than about 10 nm, a vertical dimension of the semiconductor device 100 may be too large.

As a result, a larger process window for the first contact hole 183 and the second contact hole 185 can be achieved since the second spacer 138 a and 138 b can prevent the etching process from advancing further and retain the integrity of their underlying components. Furthermore, a height H1 of the first sacrificial layers 156 a and 156 b and a height H2 of the second sacrificial layer 174 can be reduced due to the strong buffering function provided by the material of the second spacer 138 a and 138 b. Additionally, a smaller height H1 of the first sacrificial layers 156 a and 156 b and a smaller height H2 of the second sacrificial layer 174 imply a smaller height of the dummy gate electrode layers 124 a and 124 b (see FIG. 4), which have been partially replaced by the first sacrificial layers 156 a and 156 b and the second sacrificial layer 174. Therefore, a dimension of the semiconductor device 100 is able to be reduced.

Reference is made to FIG. 21. A second barrier material layer 184 is conformally formed in the first contact hole 183 (see FIG. 20) and the second contact hole 185 (see FIG. 20), and a conductive material 186 is then deposited, such as by a CVD process, a PVD process, a PECVD process, a LPCVD process, the like, or a combination thereof, to fill in the first contact hole 183 and the second contact hole 185. The second barrier material layer 184 covers exposed surfaces of the second ILD layer 182, the CESL 180, the second spacer 138 a and 138 b, the first sacrificial layer 156 a, the second sacrificial layer 174, the gate stack 150 a, the second barrier layer 144, and the bottom conductive feature 172. In some embodiments, the second barrier material layer includes, but are not limited to, cobalt (Co), silver (Ag), aluminium (Al), zinc (Zn), calcium (Ca), gold (Au), magnesium (Mg), tungsten (W), molybdenum (Mo), nickel (Ni), chromium (Cr), the like, or combinations thereof. Furthermore, the conductive material layer 186 includes, but are not limited to, titanium nitride (TiN), tantalum nitride (TaN), tantalum (Ta), titanium (Ti), hafnium (Hf), zirconium (Zr), nickel (Ni), tungsten (W), cobalt (Co), copper (Cu), aluminium (Al), the like, or combinations thereof.

Reference is made to FIG. 22. A planarization process, such as a CMP process, is performed to remove excess portions of the second barrier material layer 184 and the conductive material 186, thus resulting in a formation of the first contact plug 190 a and the second contact plug 190 b respectively in the first contact hole 183 (see FIG. 20) and the second contact hole 185 (see FIG. 20). The first contact plug 190 a penetrates through the first sacrificial layer 156 a to make an electrical contact with the gate stack 150 a, and the second contact plug 190 b penetrates through the second sacrificial layer 174 to make an electrical contact with the bottom conductive feature 172 over the source/drain region 112. As a result, the first contact plug 190 a and the second contact plug 190 b are respectively formed in a staircase configuration. More specifically, the first contact plug 190 a has an upper portion 190 a′ and a lower portion 190 a″, in which a sidewall of the upper portion 190 a′ is defined by sidewalls of the second ILD layer 182 and the CESL 180, while a sidewall of the lower portion 190 a″ is defined by sidewalls of the second spacer 138 a and the first sacrificial layer 156 a, and a diameter of the upper portion 190 a′ is larger than that of the lower portion 190 a″. Additionally, a sidewall of the lower portion 190 a″ of the first contact plug 190 a in contact with the first sacrificial layer 156 a is tilted with respect to the fin structure 110, while a sidewall of the lower portion 190 a″ of the first contact plug 190 a in contact with the second spacer 138 a is substantially straight and vertical with respect to the fin structure 110. Similarly, the second contact plug 190 b has an upper portion 190 b′ and a lower portion 190 b″, in which a sidewall of the upper portion 190 b′ is defined by sidewalls of the second ILD layer 182 and the CESL 180, while a sidewall of the lower portion 190 b″ is defined by sidewalls of the second spacer 138 b and the second sacrificial layer 174, and a diameter of the upper portion 190 b′ is larger than that of the lower portion 190 b″. Additionally, a sidewall of the lower portion 190 b″ of the first contact plug 190 b in contact with the second sacrificial layer 174 is tilted with respect to the fin structure 110, while a sidewall of the lower portion 190 b″ of the first contact plug 190 b in contact with the second spacer 138 b is substantially straight and vertical with respect to the fin structure 110. Furthermore, a bottom surface 193 a of the first contact plug 190 a and a bottom surface 193 b of the second contact plug 190 b are coplanar with bottom surfaces 139 a″ and 139 b″ of the second portions 138 a″ and 138 b″ second spacers 138 a and 138 b.

In the following descriptions, another semiconductor device and a method of forming the same will be discussed.

FIG. 23 is a flow chart illustrating a method of fabricating a semiconductor device in accordance with some embodiments of the present disclosure. The method begins with block 20 in which an interlayer dielectric layer and a gate stack are formed on a semiconductor substrate. The method continues with block 22 in which an air spacer and a first spacer are formed to surround a sidewall of the gate stack, wherein the first spacer is on a sidewall of the interlayer dielectric layer, and the air spacer is between the gate stack and the first spacer. The method continues with block 24 in which a second spacer is formed on the first spacer and the air spacer, wherein the second spacer has a portion in contact with a sidewall of the first spacer. The method continues with block 26 in which a first contact hole is formed to land on the second spacer and the gate stack, wherein a sidewall of the first contact hole is defined by the second spacer. The method continues with block 28 in which the first contact hole is filled with a conductive material.

As employed in the present disclosure, the semiconductor device 200 refers to any fin-based, multi-gate transistor. The semiconductor device 200 may be included in a microprocessor, memory cell, and/or other integrated circuit (IC). It is understood that additional processes may be provided before, during, and after the method of FIG. 23, and that some other processes may only be briefly described herein. Also, FIGS. 23 through 44 are simplified for a better understanding of the inventive concepts of the present disclosure. For example, although the figures illustrate the semiconductor device 200, it is understood the IC may include a number of other devices including resistors, capacitors, inductors, fuses, etc.

Reference is made to FIGS. 23-44, which are cross-sectional views illustrating the method for fabricating the semiconductor device 200 at various stages in accordance with some embodiments of the present disclosure.

Reference is made to FIG. 24. A substrate with a fin structure 210 is provided. The fin structure 210 is formed by etching into the substrate. In some embodiments, the substrate may be a semiconductor wafer such as a silicon wafer. Alternatively or additionally, the substrate may include elementary semiconductor materials, compound semiconductor materials, and/or alloy semiconductor materials. Examples of the elementary semiconductor materials may be, but are not limited to, crystal silicon, polycrystalline silicon, amorphous silicon, germanium, and/or diamond. Examples of the compound semiconductor materials may be, but are not limited to, silicon carbide, gallium arsenic, gallium phosphide, indium phosphide, indium arsenide, and/or indium antimonide. Examples of the alloy semiconductor materials may be, but are not limited to, SiGe, GaAsP, AlInAs, AlGaAs, GaInAs, GaInP.

Afterwards, dummy gate structures, such as a first dummy gate structure 220 a and a second dummy gate structure 220 b are formed cross over the fin structure 210. The first dummy gate structure 220 a includes a gate dielectric layer 222 a, a dummy gate electrode layer 224 a, and a hard mask 226 a. The second dummy gate structure 220 b includes a gate dielectric layer 222 b, a dummy gate electrode layer 224 b, and a hard mask 226 b. The formation of the gate dielectric layers 222 a and 222 b and the dummy gate electrode layers 224 a and 224 b includes depositing a gate dielectric material layer (not shown) over the fin structure 210, depositing a dummy gate material layer (not shown) over the gate dielectric material layer, and patterning the dummy gate material layer and the gate dielectric material layer by an etching process, in accordance with some embodiments. The gate dielectric material layer and the dummy gate material layer may be deposited using a chemical vapor deposition (CVD) process. The hard masks 226 a and 226 b are formed over portions of the dummy gate material layer during the etching process, such that portions of the gate dielectric material layer and the dummy gate material layer not covered by the hard masks 226 a and 226 b are removed. In some embodiments, the material of the gate dielectric layers 222 a and 222 b includes silicon oxide, and the material of the dummy gate electrode layer 224 a and 224 b includes polysilicon.

Reference is made to FIG. 25. Third spacers 231 a and 231 b are respectively formed on opposite sidewalls of the first and second dummy gate structures 220 a and 220 b. The third spacers 231 a and 231 b may be formed by conformally depositing a third spacer material layer (not shown) followed by an anisotropic etching (e.g., lateral etching) process. An example of the third spacer material layer may be a non-porous material including nitride. After the third spacers 231 a and 231 b are formed, low-k spacers 232 a and 232 b are respectively formed adjacent to the third spacers 231 a and 231 b. The low-k spacers 232 a and 232 b may be formed by conformally depositing a low-k spacer material layer (not shown) followed by an anisotropic etching (e.g., lateral etching) process. An example of the low-k spacer material may be a porous low-k material including SiOC, SiOCN, other suitable materials, or combinations thereof. Next, first spacers 234 a and 234 b are then respectively formed adjacent to the low-k spacers 232 a and 232 b. The first spacers 234 a and 234 b may be formed by conformally depositing a first spacer material layer (not shown) followed by an anisotropic etching (e.g., lateral etching) process. An example of the first spacer material layer may be a non-porous material including nitride. As a result, the low-k spacers 232 a and 232 b are formed between the first spacers 234 a and 234 b and the third spacers 231 a and 231 b, and the third spacers 231 a and 231 b are formed between the low-k spacers 232 a and 232 b and the first and second dummy gate structures 220 a and 220 b.

After the formation of the third spacers 231 a and 231 b, the low-k spacers 232 a and 232 b, and the first spacers 234 a and 234 b, a source/drain region 212 is formed in the substrate between the first and second dummy gate structures 220 a and 220 b. Although only one source/drain region 212 is illustrated in FIG. 25, a plurality of source/drain regions may be formed on opposite sides of the first and second dummy gate structures 220 a and 220 b. A dimension of the source/drain region 212 is defined by the first spacers 234 a and 234 b. In some embodiments, the source/drain region 212 may include the introduction of suitable dopant types, such as n-type or p-type dopants. The formation of the source/drain region 212 includes halo (or pocket) and/or low-dose drain (LDD) implantation, source/drain implantation, source/drain activation and/or other suitable processes. In other embodiments, the source/drain regions may include raised source/drain regions, strained regions, epitaxially grown regions, and/or other suitable techniques. In further embodiments, the source/drain activation process may include a rapid thermal annealing.

Reference is made to FIG. 26. A first interlayer dielectric (ILD) layer 240 is formed between the first and second dummy gate structures 220 a and 220 b, such that the first spacers 234 a and 234 b are on sidewalls of the ILD layer 240. The first ILD layer 240 may be formed by a CVD process, a high-density plasma (HDP) process, the like, or combinations thereof. In some embodiments, the first ILD layer 240 may be optionally planarized to lower its top surface to a level of first and second dummy gate structures 220 a and 220 b. For example, the first ILD layer 240 is planarized by using a chemical mechanical planarization (CMP) process. In other embodiments, other planarization techniques may be used, such as etching. The material of the first ILD layer 240 may include a dielectric material, such as a non-porous oxide material.

Reference is made to FIG. 27. The hard masks 226 a and 226 b (see FIG. 26) are removed after the first ILD layer 240 is formed. The dummy gate electrode layer 224 a and 224 b (see FIG. 26) are then removed to respectively form recesses 235 a and 235 b between the third spacers 231 a and 231 b. The removal of the dummy gate electrode layer 224 a and 224 b may be performed by a dry etching process which is selective to the material of the dummy gate electrode layer 224 a and 224 b. For example, if the dummy gate electrode layer 224 a and 224 b includes polysilicon, a dry etch using NF, SF, Cl, HBr, the like, or combinations thereof; or a wet etch using NH₄OH, tetramethylammonium hydroxide (TMAH), the like, or combinations thereof may be performed. In some embodiments, the etching of the dummy gate electrode layer 224 a and 224 b may stop at the gate dielectric layers 222 a and 222 b. As a result, the recesses 235 a and 235 b are formed to respectively expose the gate dielectric layers 222 a and 222 b. In alternative embodiments, the gate dielectric layers 222 a and 222 b may be removed along with the dummy gate electrode layer 224 a and 224 b. Diameters of the recesses 235 a and 235 b are respectively defined by sidewalls of the third spacers 231 a and 231 b.

Reference is made to FIG. 28. Gate stacks 250 a and 250 b are respectively formed in the recesses 235 a and 235 b (see FIG. 27). In some embodiments, the gate stacks 250 a and 250 b may include a single material or any combination of layers and different materials as may be appropriate. For example, the gate stacks 250 a and 250 b may include work function layers 252 a and 252 b and metal gate electrode layers 254 a and 254 b. The work function layers 252 a and 252 b and the metal gate electrode layers 254 a and 254 b are sequentially formed in the recesses 235 a and 235 b. For example, a work function material layer (not shown) is conformally formed in the recesses 235 a and 235 b covering the gate dielectric layers 222 a and 222 b and sidewalls of the third spacers 231 a and 231 b, and a metal gate electrode material layer (not shown) is then deposited, such as by a CVD process, a physical vapor deposition (PVD) process, the like, or a combination thereof, to fill in the recesses 235 a and 235 b. A planarization process, such as a CMP process, may be performed to remove excess portions of the metal gate electrode material layer and the work function material layer, in which the excess portions are over the top of the first ILD layer 240, the low-k spacers 232 a and 232 b, the first spacers 234 a and 234 b, and the third spacers 231 a and 231 b, thus resulting in a replacement of the dummy gate electrode layer 224 a and 224 b (see FIG. 26) and the hard masks 226 a and 226 b (see FIG. 26) with the gate stacks 250 a and 250 b including the work function layers 252 a and 252 b and the metal gate electrode layers 254 a and 254 b. The work function layers 252 a and 252 b may be tuned to have a proper work function. For example, if a p-type work function metal (p-metal) for a p-metal oxide semiconductor (pMOS) device is desired, p-type work function materials may be used. On the other hand, if an n-type work function metal (n-metal) for n-metal oxide semiconductor (nMOS) devices is desired, n-type work function materials may be used. The materials of the metal gate electrode layers 254 a and 254 b may include elemental metal, an alloy of metals, multiple layers of elemental metal, or combinations thereof, and can include tungsten (W), aluminium (Al), cobalt (Co), ruthenium (Ru), the like, or combinations thereof.

Reference is made to FIG. 29. The gate stacks 250 a and 250 b are etched back to a level approximately half the height of the third spacers 231 a and 231 b, the low-k spacers 232 a and 232 b, and the first spacers 234 a and 234 b. A mask layer (not shown) may be formed over the first ILD layer 240, the third spacers 231 a and 231 b, the low-k spacers 232 a and 132 b, and the first spacers 234 a and 234 b during the etching process. As a result, the recesses 235 a and 235 b are reappeared with a shallower depth, and upper portions of the third spacers 231 a and 231 b are exposed by the work function layers 252 a and 252 b of the gate stacks 250 a and 250 b.

Reference is made to FIG. 30. Upper portions of the third spacers 231 a and 231 b, upper portions of the low-k spacers 232 a and 232 b, and upper portions of the first spacers 234 a and 234 b are removed by an etching process, such as a wet etching process or a dry etching process. In some embodiments, the third spacers 231 a and 231 b, the low-k spacers 132 a and 132 b, and the first spacers 134 a and 134 b are etched back to a level higher than the gate stacks 250 a and 250 b. A mask layer (not shown) may be formed over the first ILD layer 240 during the etching process. As a result, top surfaces of the third spacers 231 a and 231 b, top surfaces of the low-k spacers 132 a and 132 b, and top surfaces of the first spacers 134 a and 134 b are coplanar. Additionally, recesses 237 a and 237 b are formed between the adjacent first ILD layers 240. The recesses 237 a and 237 b include upper portions 237 a′ and 237 b′ and lower portions 237 a″ and 237 b″, in which diameters of the upper portions 237 a′ and 237 b′ are defined by sidewalls of the adjacent first ILD layers 240, and diameters of the lower portions 237 a″ and 237 b″ are defined by sidewalls of the third spacers 231 a and 231 b. Hence, the diameters of the upper portions 237 a′ and 237 b′ of the recesses 237 a and 237 b are larger than those of the lower portions 237 a″ and 237 b″ of the recesses 237 a and 237 b.

Reference is made to FIG. 31. The remaining low-k spacers 232 a and 232 b are then removed, such that spaces 236 are formed between the third spacers 231 a and 231 b and the first spacers 234 a and 234 b, and portions of the fin structure 210 are exposed from the spaces 236. The removal of the low-k spacers 232 a and 232 b may be performed by an etching process, such as a wet etching process or a dry etching process. In some embodiments, the material of the low-k spacers 232 a and 232 b, such as SiOC or SiOCN, gives an etching selectivity relative to the material of the first ILD layer 240, the first spacers 234 a and 234 b, and the third spacers 231 a and 231 b which including oxide, nitride and nitride, respectively. In alternative embodiments, the porous material of the low-k spacers 232 a and 232 b gives an etching selectivity relative to the non-porous materials of the first ILD layer 240, the first spacers 234 a and 234 b, and the third spacers 231 a and 231 b. As a result, sidewalls of the first spacers 234 a and 234 b and sidewalls of the third spacers 231 a and 231 b are exposed from the spaces 236.

Reference is made to FIG. 32. A second spacer material 238 is conformally formed on the semiconductor structure 200 shown in FIG. 31 by deposition. For example, the second spacer material 238 covers the first ILD layer 240, the gate stacks 250 a and 250 b, the first spacers 232 a and 232 b, the spaces 236, and the third spacers 231 a and 231 b, and is formed on sidewalls of the first ILD layer 240 and sidewalls of the third spacers 231 a and 231 b. In some embodiments, the second spacer material 238 has portions 238′ embedded into the spaces 236 and in contact with sidewalls of the third spacers 231 a and 231 b and sidewalls of the first spacers 234 a and 234 b. Hence, spaces 236 are reappeared with a smaller height and are referred to as air spacers 236 a and 236 b in the following descriptions. The air spacers 236 a and 236 b having an extremely low-k characteristic are formed to reduce parasitic capacitance of the semiconductor device 200. Examples of the second spacer material 238 include, but are not limited to, high-k dielectric materials including AlO, AlN, AlON, ZrO, ZrN, ZrAlO, HfO, the like, or combinations thereof; or non-porous and low-k materials including SiO, SiN, SiC, SiCN, SiON, SiOCN, the like, or combinations thereof. Since the third spacers 231 a and 231 b are between the gate stacks 250 a and 250 b and the spaces 236, the second spacer material 238 can formed on sidewalls of the third spacers 231 a and 231 b instead of deeply filling into the spaces 236.

Since a thickness T3 of the removed low-k spacers 232 a and 232 b (see FIG. 25) is in a range from about 1 nm to about 10 nm, a width W3 of the spaces 236 (see FIG. 31) is in a range from about 1 nm to about 10 nm, and a width W3 of the air spacers 236 a and 236 b is in a range from about 1 nm to about 10 nm. In order to ensure the functionality of the air spacers 236 a and 236 b, a height of the air spacers 236 a and 236 b should not be too small, and since a length L3 of the portions 238′ of the second spacer material 238 extending into the spaces 236 affects the height of the air spacers 236 a and 236 b, the length L3 of the portions 238′ of the second spacer material 238 extending into the spaces 236 should not be too large. The length L3 of the portions 238′ of the second spacer material 238 extending into the spaces 236 is controlled by the width W3 of the spaces 236 which is in a range from about 1 nm to about 10 nm. For example, if the width W3 of the spaces 236 is larger than about 10 nm, the second spacer material 238 may easily fill in the spaces 236 at a large extent during the deposition, resulting in a decrease in height of the air spacers 236 a and 236 b, or even an entire filling-up of the spaces 236. On the other hand, if the width W3 of the spaces 236 is smaller than about 1, which means the thickness T3 of the removed low-k spacer 232 a and 232 b is smaller than about 1, the formation of the spaces 236 may be difficult since bottom portions of the low-k spacers 232 a and 232 b may be difficult to remove due to the small thickness T3. In some embodiments, the length L3 of the portions 238′ of the second spacer material 238 extending into the spaces 136 is in a range from about 0.5 nm to about 5 nm to ensure that the height of the air spacers 236 a and 236 b is in an appropriate range to maintain their functionality (i.e., to reduce parasitic capacitance of the semiconductor device 200). As a result, a height of the air spacers 236 a and 236 b is larger than a height of the gate stacks 250 a and 250 b.

Reference is made to FIG. 33. An etching process such as a wet etching process is performed, such that portions of the second spacer material 238 (see FIG. 22) are removed. For example, portions of the second spacer material 238 covering the gate stacks 250 a and 250 b and the first ILD layer 240 are removed, and portions of the second spacer material 238 on the sidewalls of the third spacers 231 a and 231 b are also removed. As a result, second spacers 238 a and 238 b are formed standing on the first spacers 232 a and 232 b, the air spacers 236 a and 236 b, and the third spacers 231 a and 231 b, and recesses 239 a and 239 b are respectively formed between the second spacers 238 a and 238 b and between the third spacers 231 a and 231 b, that is, diameters of the recesses 239 a and 239 b are respectively defined by sidewalls of the second spacers 238 a and 238 b and respectively defined by sidewalls of the third spacers 231 a and 231 b. The gate stacks 250 a and 250 b are exposed by the third spacers 231 a and 231 b, and top surfaces of the second spacers 238 a and 238 b are coplanar with the top surface of the first ILD layer 240. In some embodiments, a thickness T4 of the second spacers 238 a and 238 b is in a range from about 1 nm to about 10 nm. Furthermore, the thickness T4 of the second spacers 238 a and 238 b should be larger than the width W3 of air spacers 236 a and 236 b to ensure the air spacers 236 a and 236 b being entirely sealed. If the thickness T4 of the second spacers 238 a and 238 b is smaller than about 1 nm, the air spacers 236 a and 236 b may possibly be exposed, resulting in a fragile structure of the semiconductor device 100; if the thickness T4 of the second spacers 138 a and 138 b is larger than about 10 nm, the size of the semiconductor device 200 would be increased accordingly.

After this step, the second spacers 238 a and 238 b including first portions 238 a′ and 238 b′ and second portions 238 a″ and 238 b″ are formed. The first portions 238 a′ and 238 b′ are the portions 238′ of the second spacer material 238 extending into the spaces 236 (see FIG. 30) and are in contact with sidewalls of the first spacers 234 a and 234 b and sidewalls of the third spacers 231 a and 231 b. The second portions 238 a″ and 238 b″ are on the first portions 238 a′ and 238 b′ of the second spacers 238 a and 238 b, the first spacers 234 a and 234 b, and the third spacers 231 a and 231 b.

Reference is made to FIG. 34. A first sacrificial material layer 256 is deposited over the semiconductor structure 200 shown in FIG. 33 by, for example, a CVD process, a plasma enhanced chemical vapor deposition (PECVD) process, the like, or combinations thereof. For example, the first sacrificial material layer 256 is filled in the recesses 239 a and 239 b (see FIG. 33), and formed over the second spacers 238 a and 238 b and the first ILD layer 240. The material of the first sacrificial material layer 256 may include a porous and low-k material. Examples of the porous and low-k material are, but are not limited to, SiO, SiN, SiC, SiCN, SiON, SiOCN, the like, or combinations thereof. Such a material give an etching selectivity relative to the materials of the second spacers 238 a and 238 b (i.e., the second spacer material 238), which include, but are not limited to, high-k dielectric materials including AlO, AlN, AlON, ZrO, ZrN, ZrAlO, HfO, the like, or combinations thereof; or non-porous and low-k materials including SiO, SiN, SiC, SiCN, SiON, SiOCN, the like, or combinations thereof.

Reference is made to FIG. 35. A planarization process is performed to lower the first sacrificial material layer 256 and to expose the second spacers 238 a and 238 b. In some embodiments, the first sacrificial material layer 256 is planarized by using a CMP process. In other embodiments, other planarization techniques may be used, such as etching. As a result, first sacrificial layers 256 a and 256 b are respectively formed in the recesses 239 a and 239 b (see FIG. 33), and are respectively formed between the second spacers 238 a and 238 b and respectively between the third spacers 231 a and 231 b. Additionally, top surfaces of the first sacrificial layers 256 a and 256 b are coplanar with top surfaces of the second spacers 238 a and 238 b and the top surface of the first ILD layer 240. Furthermore, the third spacers 231 a and 231 b respectively extend along sidewalls of the first sacrificial layers 256 a and 256 b.

Reference is made to FIG. 36. The first ILD layer 240 is removed by an etching process. A mask layer (not shown) may be formed over the first sacrificial layer 256 a and 256 b and the second spacers 238 a and 238 b during the etching process. The removal of the first ILD layer 240 results in a formation of a recess 242 above the underlying source/drain region 212, that is, an exposure of the underlying source/drain region 212 from the recess 242.

Reference is made to FIG. 37. A first barrier layer 244 and a bottom conductive feature 272 are sequentially formed in the recess 242 (see FIG. 36). In some embodiments, a first barrier material layer (not shown) is conformally formed in the recess 242 covering the source/drain region 212, sidewalls of the first spacers 234 a and 234 b, and sidewalls of the second spacers 138 a and 138 b, and a bottom conductive material (not shown) is then deposited, such as by a CVD process, a PVD process, a PECVD process, a low pressure CVD (LPCVD) process, the like, or a combination thereof, to fill in the recess 242. A planarization process, such as a CMP process, may be performed to remove excess portions of the first barrier material layer and the bottom conductive material, and thus resulting in a replacement of the first ILD layer 240 with the first barrier layer 244 and the bottom conductive feature 272. In some embodiments, the first barrier material layer includes, but are not limited to, cobalt (Co), silver (Ag), aluminium (Al), zinc (Zn), calcium (Ca), gold (Au), magnesium (Mg), tungsten (W), molybdenum (Mo), nickel (Ni), chromium (Cr), the like, or combinations thereof. Additionally, the bottom conductive material includes conductive materials, such as tungsten (W), aluminium (Al), cobalt (Co), ruthenium (Ru), the like, or combinations thereof, which form an electrical connection to the source/drain region 212. In some embodiments, other layers such as a work function layer and/or a capping layer may be formed in the recess 242, but the present disclosure is not limited in this regard.

Reference is made to FIG. 38. The first barrier layer 244 and the bottom conductive feature 272 are etched back. A mask layer (not shown) may be formed over the first sacrificial layers 256 a and 256 b and the second spacers 238 a and 238 b during the etching process. As a result, a recess 246 is formed over the first barrier layer 244 and the bottom conductive feature 272, and a diameter of the recess 246 is defined by the sidewalls of the second spacers 238 a and 238 b and sidewalls of the third spacers 231 a and 231 b. In some embodiments, a top surface of the bottom conductive feature 272 is coplanar with the top surfaces of the gate stacks 250 a and 250 b. In alternative embodiments, the top surface of the bottom conductive feature 272 is higher or lower than the top surfaces of the gate stacks 250 a and 250 b. Since the air spacers 236 a and 236 b are between the bottom conductive feature 272 and the gate stacks 250 a and 250 b, the air spacers 236 a and 236 b with an extremely low-k characteristic can effectively reduce the parasitic capacitance between the gate stacks 250 a and 250 b and the bottom conductive features 272.

Reference is made to FIG. 39. A second sacrificial material layer (not shown) is deposited over the semiconductor structure 200 shown in FIG. 38 by, for example, a CVD process, a PECVD process, the like, or combinations thereof. For example, the second sacrificial material layer is filled in the recess 246 (see FIG. 38), and formed over the second spacers 238 a and 238 b and the first sacrificial layers 256 a and 256 b. After that, a planarization process is then performed to lower the second sacrificial material layer and to expose the second spacers 238 a and 238 b and the first sacrificial layers 256 a and 256 b. In some embodiments, the second sacrificial material layer is planarized by using a CMP process. In other embodiments, other planarization techniques may be used, such as etching. As a result, a second sacrificial layer 274 is formed in the recess 246 to cover the bottom conductive feature 272 and the first barrier layer 244. A top surface of the second sacrificial layer 274 is coplanar with top surfaces of the second spacers 238 a and 238 b and top surfaces of the first sacrificial layers 256 a and 256 b. The material of the second sacrificial layer 274 (i.e., second sacrificial material layer) may include a porous and low-k material. Examples of the porous and low-k material are, but are not limited to, SiO, SiN, SiC, SiCN, SiON, SiOCN, the like, or combinations thereof. Such a material give an etching selectivity relative to the materials of the second spacers 238 a and 238 b (i.e., the second spacer material 238), which include, but are not limited to, high-k dielectric materials including AlO, AlN, AlON, ZrO, ZrN, ZrAlO, HfO, the like, or combinations thereof; or non-porous and low-k materials including SiO, SiN, SiC, SiCN, SiON, SiOCN, the like, or combinations thereof.

Reference is made to FIG. 40. A contact etch stop layer (CESL) 280 and a second ILD layer 282 are formed to blanket cover the first sacrificial layers 256 a and 256 b, the second sacrificial layer 274, and the second spacers 238 a and 238 b by a deposition process such as, for example, a CVD process, a PECVD process, a LPCVD process, the like, or a combination thereof. The material of the contact etch stop layer 280 includes, for example, SiO, SiN, SiC, SiCN, SiON, SiOCN, the like, or combinations thereof. Such a material give an etching selectivity relative to the materials of the second spacers 238 a and 238 b (i.e., the second spacer material 238), which include, but are not limited to, high-k dielectric materials including AlO, AlN, AlON, ZrO, ZrN, ZrAlO, HfO, the like, or combinations thereof; or non-porous and low-k materials including SiO, SiN, SiC, SiCN, SiON, SiOCN, the like, or combinations thereof. Additionally, the material of the second ILD layer 282 may include the same material as the material of the first ILD layer 240, which will not be repeated hereinafter.

Reference is made to FIG. 41. A first contact hole 283 is formed penetrating through the second ILD layer 282, the CESL 280, and the first sacrificial layer 256 a. The first contact hole 183 may be formed using acceptable photolithography and non-isotropic etching techniques, such as a reactive-ion etching (RIE), by removing portions of the second ILD layer 282, the CESL 280, and the first sacrificial layer 256 a. Since the second spacers 238 a have an etching selectivity in a range from about 10 to about 30 relative to the CESL 280 and the first sacrificial layer 256 a, the etching process may stop at the second spacers 238 a to prevent a further removal of the second spacers 238 a and the underlying third spacers 231 a. Furthermore, since the removal is performed by a non-isotropic etching process without any lateral etching, a sidewall of the third spacer 231 a exposed from the first contact hole 283 is able to be retained and remained substantially straight. Hence, the first contact hole 283 is formed to expose a portion of the top surface of the gate stack 250 a, a portion of the top surface of the second spacer 238 a, a portion of the sidewall of the second spacer 138 a, and a portion of the sidewall of the third spacers 231 a, resulting in a staircase configuration of the first contact hole 283. Stated differently, the first contact hole 283 has an upper portion 283 a and a lower portion 283 b, in which a diameter of the upper portion 283 a is larger than that of the lower portion 283 b, and a sidewall of the lower portion 283 b of the first contact hole 283 is defined by the sidewall of the second spacers 238 a and the sidewall of the third spacers 231 a. Furthermore, a sidewall of the second ILD layer 282 is coplanar with a sidewall of the CESL 280 and a sidewall of the first sacrificial layer 256 a.

Reference is made to FIG. 42. A second contact hole 285 is formed penetrating through the second ILD layer 282, the CESL 280, and the second sacrificial layer 274. The second contact hole 285 may be formed using acceptable photolithography and non-isotropic etching techniques, such as a reactive-ion etching (RIE), by removing portions of the second ILD layer 282, the CESL 280, and the second sacrificial layer 274. Since the second spacers 238 b have an etching selectivity in a range from about 10 to about 30 relative to the CESL 280 and the second sacrificial layer 274, the etching process may stop at the second spacers 238 b to prevent a further removal of the second spacers 238 b and the underlying third spacers 231 b. Furthermore, since the removal is performed by a non-isotropic etching process without any lateral etching, a sidewall of the first spacer 234 b exposed from the second contact hole 285 is able to be retained and remained substantially straight. Hence, the second contact hole 285 is formed to expose a portion of the top surface of the bottom conductive feature 272, a portion of the top surface of the first barrier layer 244, a portion of the top surface of the second spacers 238 b, a portion of the sidewall of the second spacers 138 b, and a portion of the sidewall of the third spacers 231 b, resulting in a staircase configuration of the second contact hole 285. Stated differently, the second contact hole 285 has an upper portion 285 a and a lower portion 285 b, in which a diameter of the upper portion 285 a is larger than that of the lower portion 285 b, and a sidewall of the lower portion 285 b of the second contact hole 285 is defined by the sidewall of the second spacers 138 b and the sidewall of the first spacers 234 b. Furthermore, a sidewall of the second ILD layer 282 is coplanar with a sidewall of the CESL 280 and a sidewall of the second sacrificial layer 274.

Since the second spacers 238 a and 238 b has an etching selectivity in a range from about 10 to about 30 relative to the CESL 280, the first sacrificial layers 256 a and 256 b, and the second sacrificial layer 274, the first contact hole 283 and the second contact hole 285 do not penetrate through the second spacers 238 a and 238 b. Hence, the first spacers 234 a and 234 b and the air spacers 136 a and 136 b are not exposed and are well protected during the etching process due to the etching resistance provided by the second spacer 238 a and 238 b. If the etching selectivity of second spacer 238 a and 238 b relative to the CESL 280, the first sacrificial layers 256 a and 256 b, and the second sacrificial layer 274 is smaller than about 10, the etching process may lead to unwanted consumption of the underlying components, such as the third spacers 231 a and 231 b, the first spacers 234 a and 234 b, and the air spacers 136 a and 136 b, thereby causing a risk for the first contact plug and the second contact plug (which will be formed respectively in the first contact hole 283 and the second contact hole 285 in subsequent steps) to be respectively in contact with the bottom conductive feature 272 and the gate stack 250 b, hence enhancing a chance for shorting.

Additionally, the length L4 of the second portions 238 a″ and 238 b″ of the second spacers 238 a and 238 b which is in a range from about 1 nm to about 10 nm also contributes to the formation of the first contact hole 283 and the second contact hole 285. Specifically, if the length L4 of the second portions 238 a″ and 238 b″ of the second spacers 238 a and 238 b is smaller than about 1 nm, the etching process may easily lead to unwanted consumption of the underlying components, such as the third spacers 231 a and 231 b, the first spacers 234 a and 234 b, and the air spacers 136 a and 136 b, thereby causing a risk for the first contact plug and the second contact plug (which will be formed respectively in the first contact hole 283 and the second contact hole 285 in subsequent steps) to be respectively in contact with the bottom conductive feature 272 and the gate stack 250 b, hence enhancing a chance for shorting. On the other hand, if the length L4 of the second portions 238 a″ and 238 b″ of the second spacers 238 a and 238 b is larger than about 10 nm, a vertical dimension of the semiconductor device 200 may be too large.

As a result, a larger process window for the first contact hole 283 and the second contact hole 285 can be achieved since the second spacer 238 a and 238 b can prevent the etching process from advancing further and retain the integrity of their underlying components. Furthermore, a height H3 of the first sacrificial layers 256 a and 256 b and a height H4 of the second sacrificial layer 274 can be reduced due to the strong buffering function provided by the material of the second spacer 238 a and 238 b. Additionally, a smaller height H3 of the first sacrificial layers 256 a and 256 b and a smaller height H4 of the second sacrificial layer 174 imply a smaller height of the dummy gate electrode layers 224 a and 224 b (see FIG. 26), which have been partially replaced by the first sacrificial layers 256 a and 256 b and the second sacrificial layer 274. Therefore, a dimension of the semiconductor device 200 is able to be reduced.

Reference is made to FIG. 43. A second barrier material layer 284 is conformally formed in the first contact hole 283 (see FIG. 42) and the second contact hole 285 (see FIG. 42), and a conductive material 286 is then deposited, such as by a CVD process, a PVD process, a PECVD process, a LPCVD process, the like, or a combination thereof, to fill in the first contact hole 283 and the second contact hole 285. The second barrier material layer 284 covers exposed surfaces of the second ILD layer 282, the CESL 280, the second spacer 238 a and 238 b, the third spacers 231 a and 231 b, the first sacrificial layer 256 a, the second sacrificial layer 274, the gate stack 250 a, the second barrier layer 244, and the bottom conductive feature 272. In some embodiments, the second barrier material layer 284 includes, but are not limited to, cobalt (Co), silver (Ag), aluminium (Al), zinc (Zn), calcium (Ca), gold (Au), magnesium (Mg), tungsten (W), molybdenum (Mo), nickel (Ni), chromium (Cr), the like, or combinations thereof. Furthermore, the conductive material layer 286 includes, but are not limited to, titanium nitride (TiN), tantalum nitride (TaN), tantalum (Ta), titanium (Ti), hafnium (Hf), zirconium (Zr), nickel (Ni), tungsten (W), cobalt (Co), copper (Cu), aluminium (Al), the like, or combinations thereof.

Reference is made to FIG. 44. A planarization process, such as a CMP process, is performed to remove excess portions of the second barrier material layer 284 and the conductive material 286, thus resulting in a formation of the first contact plugs 290 a and the second contact plug 290 b respectively in the first contact hole 283 (see FIG. 42) and the second contact hole 285 (see FIG. 42). The first contact plug 290 a penetrates through the first sacrificial layer 256 a to make an electrical contact with the gate stack 250 a, and the second contact plug 290 b penetrates through the second sacrificial layer 274 to make an electrical contact with the bottom conductive feature 272 over the source/drain region 212. As a result, the first contact plug 290 a and the second contact plug 290 b are respectively formed in a staircase configuration. More specifically, the first contact plug 290 a has an upper portion 290 a′ and a lower portion 290 a″, in which a sidewall of the upper portion 290 a′ is defined by sidewalls of the second ILD layer 282 and the CESL 280, while a sidewall of the lower portion 290 a″ is defined by sidewalls of the second spacers 238 a, the third spacers 231 a, and the first sacrificial layer 156 a, and a diameter of the upper portion 290 a′ is larger than that of the lower portion 290 a″. Additionally, a sidewall of the lower portion 290 a″ of the first contact plug 290 a in contact with the first sacrificial layer 256 a is tilted with respect to the fin structure 210, while a sidewall of the lower portion 290 a″ of the first contact plug 290 a in contact with the second spacer 238 a and the third spacer 231 a is substantially straight and vertical with respect to the fin structure 210. Similarly, the second contact plug 290 b has an upper portion 290 b′ and a lower portion 290 b″, in which a sidewall of the upper portion 290 b′ is defined by sidewalls of the second ILD layer 282 and the CESL 280, while a sidewall of the lower portion 290 b″ is defined by sidewalls of the second spacer 238 b, the first spacers 234 b, and the second sacrificial layer 274, and a diameter of the upper portion 290 b′ is larger than that of the lower portion 290 b″. Additionally, a sidewall of the lower portion 290 b″ of the first contact plug 290 b in contact with the second sacrificial layer 274 is tilted with respect to the fin structure 210, while a sidewall of the lower portion 290 b″ of the first contact plug 290 b in contact with the second spacer 238 b and the first spacer 234 b is substantially straight and vertical with respect to the fin structure 210.

Based on the aforementioned descriptions, various advantages may be provided by the present disclosure. More specifically, since the second spacers have an etching selectivity relative to the first sacrificial layer, second sacrificial layer, and the contact etch stop layer, the second spacers have the capability to endure the etching treatment and therefore protect the underlying components, such as the first spacers, the air spacers, and the third spacers during the contact hole formation process. As such, the overall height of the gate stack is reduced due to the strong buffering function provided by the second spacers. Additionally, the air spacers with an extremely low-k characteristic can effectively reduce the parasitic capacitance between the gate stacks and the bottom conductive features, thus enhancing the performance of the semiconductor device.

In some embodiments, a semiconductor device includes a semiconductor substrate, a gate stack, an air spacer, a first spacer, a second spacer, a sacrificial layer, and a contact plug. The gate stack is on the semiconductor substrate. The air spacer is around the gate stack. The first spacer is around the air spacer. The second spacer is on the air spacer and the first spacer. The sacrificial layer is on the gate stack, and an etching selectivity between the second spacer and the sacrificial layer is in a range from about 10 to about 30. The contact plug lands on the second spacer and the gate stack.

In some embodiments, a semiconductor device includes a semiconductor substrate, a gate stack, an air spacer, a first spacer, a second spacer, a third spacer, and a first sacrificial layer. The gate stack is on the semiconductor substrate. The air spacer is around the gate stack. The first spacer is around the air spacer. The second spacer is on the air spacer and the first spacer. The third spacer is between the gate stack and the air spacer. The first sacrificial layer is on the gate stack, and the third spacer extends along a sidewall of the first sacrificial layer.

In some embodiments, a method of fabricating a semiconductor device including: forming an interlayer dielectric layer and a gate stack on a semiconductor substrate; forming an air spacer and a first spacer surrounding a sidewall of the gate stack, wherein the first spacer is on a sidewall of the interlayer dielectric layer, and the air spacer is between the gate stack and the first spacer; forming a second spacer on the first spacer and the air spacer, wherein the second spacer has a portion in contact with a sidewall of the first spacer; forming a first contact hole landing on the second spacer and the gate stack, wherein a sidewall of the first contact hole is defined by the second spacer; and filling the first contact hole with a conductive material.

The foregoing outlines features of several embodiments so that those skilled in the art may better understand the aspects of the present disclosure. Those skilled in the art should appreciate that they may readily use the present disclosure as a basis for designing or modifying other processes and structures for carrying out the same purposes and/or achieving the same advantages of the embodiments introduced herein. Those skilled in the art should also realize that such equivalent constructions do not depart from the spirit and scope of the present disclosure, and that they may make various changes, substitutions, and alterations herein without departing from the spirit and scope of the present disclosure. 

What is claimed is:
 1. A semiconductor device, comprising: a semiconductor substrate; a gate stack on the semiconductor substrate; an air spacer around the gate stack; a first spacer around the air spacer; a second spacer on the air spacer and the first spacer; a sacrificial layer on the gate stack, wherein an etching selectivity between the second spacer and the sacrificial layer is in a range from about 10 to about 30; and a contact plug landing on the second spacer and the gate stack.
 2. The semiconductor device of claim 1, wherein a height of the air spacer is smaller than a height of the gate stack.
 3. The semiconductor device of claim 1, wherein the second spacer has a portion in contact with a sidewall of the gate stack.
 4. The semiconductor device of claim 1, wherein a width of the air spacer is in a range from about 1 nm to about 10 nm.
 5. The semiconductor device of claim 1, wherein the second spacer comprises a high-k dielectric material.
 6. The semiconductor device of claim 1, wherein the second spacer comprises a non-porous and low-k dielectric material.
 7. A semiconductor device, comprising: a semiconductor substrate; a gate stack on the semiconductor substrate; an air spacer around the gate stack; a first spacer around the air spacer; a second spacer on the air spacer and the first spacer; a third spacer between the gate stack and the air spacer; and a first sacrificial layer on the gate stack, wherein the third spacer extends along a sidewall of the first sacrificial layer.
 8. The semiconductor device of claim 7, wherein the second spacer is on the third spacer.
 9. The semiconductor device of claim 7, wherein a height of the air spacer is larger than a height of the gate stack.
 10. The semiconductor device of claim 7, further comprising a bottom conductive structure on the semiconductor substrate, wherein the air spacer, the first spacer, and the third spacer are between the bottom conductive structure and the gate stack.
 11. The semiconductor device of claim 10, further comprising a second sacrificial layer on the bottom conductive structure, wherein an etching selectivity between the second spacer and the second sacrificial layer is in a range from about 10 to about
 30. 12. The semiconductor device of claim 7, further comprising: an etch stop layer on the first sacrificial layer and the second spacer; and an interlayer dielectric layer on the etch stop layer, wherein a sidewall of the interlayer dielectric layer is coplanar with a sidewall of the etch stop layer and a sidewall of the first sacrificial layer.
 13. A method of fabricating a semiconductor device, comprising: forming an interlayer dielectric layer and a gate stack on a semiconductor substrate; forming an air spacer and a first spacer surrounding a sidewall of the gate stack, wherein the first spacer is on a sidewall of the interlayer dielectric layer, and the air spacer is between the gate stack and the first spacer; forming a second spacer on the first spacer and the air spacer, wherein the second spacer has a portion in contact with a sidewall of the first spacer; forming a first contact hole landing on the second spacer and the gate stack, wherein a sidewall of the first contact hole is defined by the second spacer; and filling the first contact hole with a conductive material.
 14. The method of claim 13, wherein forming the air spacer and the first spacer surrounding the sidewall of the gate stack comprises: forming a low-k spacer and a first spacer surrounding the sidewall of the gate stack; removing a top portion of the low-k spacer and a top portion of the first spacer, such that a top surface of the gate stack is coplanar with a top surface of the first spacer and a top surface of the first spacer; and replacing the low-k spacer with the air spacer.
 15. The method of claim 13, wherein forming the second spacer on the first spacer and the air spacer comprises: depositing a second spacer material on the gate stack, the first spacer, a space between the gate stack and the first spacer, and the interlayer dielectric layer, and on a sidewall of the interlayer dielectric layer, wherein a portion of the second spacer material is embedded into the space and in contact with a sidewall of the gate stack; and removing portions of the second spacer material on the gate stack and the interlayer dielectric layer.
 16. The method of claim 13, further comprising: forming a third spacer surrounding the sidewall of the gate stack, wherein the third spacer is between the air spacer and the gate stack, a portion of the second spacer is on the third spacer, and a portion of the second spacer is in contact with a sidewall of the third spacer.
 17. The method of claim 16, wherein the sidewall of the first contact hole is further defined by the third spacer.
 18. The method of claim 16, wherein forming the second spacer on the first spacer, the air spacer, and the third spacer comprises: depositing a second spacer material on the gate stack, the first spacer, the third spacer, a space between the first spacer and the third spacer, and the interlayer dielectric layer, and on a sidewall of the interlayer dielectric layer and a sidewall of the third spacer, wherein a portion of the second spacer material is embedded into the space and in contact with a sidewall of the third spacer; and removing portions of the second spacer material on the gate stack and the interlayer dielectric layer, and on the sidewall of the third spacer.
 19. The method of claim 16, wherein forming the air spacer, the first spacer, and the third spacer surrounding the sidewall of the gate stack comprises: forming the first spacer, a low-k spacer, and a third spacer surrounding the sidewall of the gate stack, wherein the low-k spacer is between the first spacer and the third spacer; removing a top portion of the first spacer, a top portion of the low-k spacer, and a top portion of the third spacer, such that a top surface of the first spacer, a top surface of the low-k spacer, and a top surface of the third spacer are higher than a top surface of the gate stack; and replacing the low-k spacer with the air spacer.
 20. The method of claim 16, further comprising: replacing the interlayer dielectric layer with a bottom conductive structure; removing a top portion of the bottom conductive structure, such that a top surface of the bottom conductive structure is coplanar with a top surface of the gate stack; forming a second contact hole landing on the second spacer and the bottom conductive structure, wherein a sidewall of the second contact hole is defined by the first spacer and the second spacer; and filling the second contact hole with the conductive material. 